Basic Info.
Model NO.
LT-PGW
Thickness
0.17mm, 0.2mm, 0.25mm, 0.3mm, 0.32mm
Raw Material
Fiber Glass Yarn + Unsaturated Polyester Rein
Package
50~200 Meters Per Roll
Thermal Grade
F, H Grade
Type
Solid
Chemistry
Inorganic Insulation
Classification
Inorganic Insulation Material
Certification
ISO9001
Brand
Lontom
Transport Package
Spool
Specification
RoHS
Trademark
LONTOM
Origin
Shanghai, China
HS Code
70199000
Production Capacity
1000000 Rolls Per Month
Product Description
Electric Insulating Edge Banding Tape
1.Thickness:0.2~0.5mm
2.Fiberglass banding tape
3.Self-adhesive insulation tape
4.SGS,RoHS
The banding tapes are of high quality, which consist of parallel twisted E-glass yarns preimpregnated with a special thermosetting polyester resin and manufactured with the proprietory technology and advanced equipments.
It's widely used in AC. DC motors, generators and transformers especially in traction motors.
Main Properties:
1.Thickness: 0.20mm±10%,0.30mm±10%
2.Width: 10mm~50mm±10%
3.Length/Spool: 50~200 meters
4.Standard color: White
5.Thermal Grade: F grade(155ºC)
H grade(180ºC)
6.Curing condition (Time to bring the piece to the temperature is not considered)
7.Storage Stability:
1.Thickness:0.2~0.5mm
2.Fiberglass banding tape
3.Self-adhesive insulation tape
4.SGS,RoHS
The banding tapes are of high quality, which consist of parallel twisted E-glass yarns preimpregnated with a special thermosetting polyester resin and manufactured with the proprietory technology and advanced equipments.
It's widely used in AC. DC motors, generators and transformers especially in traction motors.
Main Properties:
1.Thickness: 0.20mm±10%,0.30mm±10%
2.Width: 10mm~50mm±10%
3.Length/Spool: 50~200 meters
4.Standard color: White
5.Thermal Grade: F grade(155ºC)
H grade(180ºC)
6.Curing condition (Time to bring the piece to the temperature is not considered)
| Temperature | ºC | 160 | 150 | 135 | 120 | 115 |
| Time | hour | 2.5 | 3 | 5 | 14 | 20 |
7.Storage Stability:
| Storage temperature | ºC | 10 | 15 | 20 | 30 |
| Time | Month | 20 | 15 | 10 | 6 |
Technical Data:
| Test content | Unit | Standard Value | ||
| Thermal class | H | F | ||
| Volatile content | % | ≤ 2 | ||
| Loss of weight at calcination | % | 26±2 | ||
| Soluble resin content | % | ≥ 90 | ||
| Tensile strength before curing | N/cm | ≥1500 | ≥1000 | |
| Maximum pull while banding | N/cm | 800 | 800 | |
| Tensile strength of ringlike sample at room temperature after curing | Mpa | 20ºC | ||
| above :900 | above :900 | |||
| Tensile strength of ringlike sample at working temperature after curing | Mpa | 180ºC | 150ºC | |
| ≥600 | ≥560 | |||
| Proof tracking index | ≥500V | |||
| Arc resistance | S | ≥160 | ||
| Breakdown voltage parallel to layers | KV | normal condition:≥25 after soaked in water for 24 hours:≥10 | ||
| Thermosetting | OK | |||
| Loss of tensile strength after soaked in oil | ≤10% | |||
Package: