Basic Info.
Model NO.
H200
Thickness
0.3mm
Width
20mm, 25mm, 50mm
Volatile Matter Content
Less Then 5%
Resin Content
26%+/-2%
Soluble Resin Content
Over 90%
Tensile Strength Before Curing
Over 1000n/Cm
Maximum Pull While Banding
Over 800n/Cm
Transport Package
by Roll
Specification
A grade
Origin
China
HS Code
7019909000
Production Capacity
3000 0000m/Y
Product Description
Banding tapes are of high quality, which consist of parallel twisted E- Glass yarns preimpregnated with a special thermosetting polyester resin.
Characters and Applications:
Class H(180 celsiuse degree) insulating material, high tensile strength, high resistance to shocks, high modulus of elasticity, dimensional stability. Widely used as ideal banding materials for electrical motors, transformers and lighting arresters.
Type:H200-W
| Item | Unit | Specification | Test data | Test Condition |
| Volatile Content(75ºC±2ºC/lh) | % | ≤2 | 1.22 | GB/T22471.2-2008 |
| Resin Content | % | 27±2 | 28.8 | |
| Soluble Resin Content(Toluen, ethanol = 3:2 solvent heat to 30 to 50ºC soaked 30 min, secondly soaked at this temperature for 15 min, then rinse with alcohol, roast 155ºC for 1h) | % | ≥90 | 95.2 | |
| Settability(155ºC±2ºC/2h) | - | Easy to peel and not sticky | meet the requirement | |
| Tensile Strength(Ring Test Speciment) Normalcy | Mpa | ≥900 | 1445 | |
| Tensile Strength(Ring Test Speciment) 200ºC±2ºC/30min | Mpa | ≥560 | 879 | |
| Tensile Modulus Of Elasticity(Ring Test Speciment) | Mpa | ≥4.5×104 | 8.46×104 |